The imaginary part of permittivity ldquo and dielectric loss tan

Fig. 12. (a & b). Experimental and simulated (thin solid line) using Zview of the complex impedance diagrams measured at selected temperatures for Co0.2Ni0.3Zn0.5Fe2O sintered at different temperatures under 517 MPa.Figure optionsDownload full-size imageDownload as PowerPoint slide
Table 4.
Equivalent circuit characteristics measured at selected temperatures for Co0.2Ni0.3Zn0.5Fe2O4 pellets sintered at different temperatures under LY2886721 pressure of 517 MPa.Sintering temperature (K)Porosity (%)Tm =523Tm =548Tm =573Tm =598Tm =673773Rs(Ω)6763162279553550R1(Ω) phylogeny 1021000402145604CPE1(μF)0.010.100.600.020.03α10.780.750.800.820.81R2(Ω) x1022504527162CPE2(μF)1.21101010α20.60110.30.2897349Rs(Ω)229686772759796R1(Ω) x102630130110553CPE1( μF)1.002310.0060.50α10.900.950.900.870.70R2(Ω) x1021204018111CPE2( μF)0.275000.00290.50α20.350.380.350.520.74117340Rs(Ω)134273463678626R1(Ω) x104100024880365CPE1( μF)4.665111α10.800.820.920.950.96127318Rs(Ω)9919104131334R1(Ω) x104470160806810CPE1( nF)1040.21103103α10.920.940.920.900.94Full-size tableTable optionsView in workspaceDownload as CSV