Fig shows typical SEM images

Fig. 3. DSC analysis results for McN 5652 melt-spun ribbon obtained at wheel speed of 35 m s−1 using continuous heating mode with the heating rates of 5–40 K min−1.Figure optionsDownload full-size imageDownload as PowerPoint slide
Table 2.
Thermal values obtained from DSC curves for melt-spun Cu50Zr40Ni5Ti5 amorphous ribbons produced at wheel speed of 35 m s−1 at different heating rates.? (K/min)Tg (K)Tx (K)ΔTx (K)Tp (K)566571449722106737245173220678731537404068273654745Full-size tableTable optionsView in workspaceDownload as CSV
Fig. 4. Kissinger plots of the amorphous Cu50Zr40Ni5Ti5 alloy manufactured at wheel speed of 35 m s−1.Figure optionsDownload full-size imageDownload as PowerPoint slide
Fig. 5. Typical XRD spectrum of the melt-spun ribbon of Cu50Zr40Ni5Ti5 alloy prepared at a follicle-stimulating hormone (FSH) wheel speed of 35 m s−1 and annealed in the temperature range of 200–800 °C for 30 min.Figure optionsDownload full-size imageDownload as PowerPoint slide